SCH 40 316 316L Stainless Steel Butt Weld Pipe

SCH 40 316 316L Stainless Steel Butt Weld Pipe

Compared with 316, the carbon content of 316L is less than 0.04%, and the carbon content of 316 is 0.08%. Carbon is easy to combine with chromium in stainless steel welding, resulting in local chromium deficiency, sensitization, contact with corrosive media, such as chloride ions, corrosion occurs.

ingenuity

• Drawing film
• Mirror 8K
• knurling
• The shear plate is bent
• Laser cutting
• punching
• Welding process
• Roll plate and strip
• Pickling process

product use

• boats
• aviation
• Chemical engineering
• electricity
• CARS
• Mine field
• Air supply
• Nuclear power

SA312 Tp316L Equivalent

UNS Designation & International Equivalent
Type	UNS	JIS	EN/DIN	EN/BS	EN/NF	ISO	GB	GOST
316L	S31603	SUS316L	X2CrNiMo18-14-3	316S13	X2CrNiMo17-12-2	19	00Cr17Ni14Mo2	03KH17H14M2

Physical Properties Of Stainless Steel 316L Tube

Grade	Density (kg/m3)	Elastic Modulus (GPa)	Mean Coefficient of Thermal Expansion (m/m/0C)			Thermal Conductivity (W/m.K)		Specific Heat 0-1000C (J/kg.K)	Electrical Resistivity (n.m)
			0-100°C	0-315°C	0-538°C	at 100°C	at 500°C
316L	8000	193	15.9	16.2	17.5	16.3	21.5	500	740

Mechanical Properties Of SS 316L Seamless Pipe

Grade	Tensile
	Ultimate/Min		Yield/Min		Elongation/Min
	KSI	MPA	KSI	MPA	%
316L	70	485	25	170	35

ASTM A312 Tp 316L Chemical Composition

Weight %	C	Mn	P	S	Si	Cr	Ni	Mo
316L	.035	2.00	.045	.030	1.00	16.0-18.0	10.0-14.0	2.0-3.0

 

 

Packing & Delivery

Product Application

 

 

Test & Certificate

Stainless Steel Pipe Service

ANGLE DISPLAY

Product Inspection

Hot Tags: sch 40 316 316l stainless steel butt weld pipe, China sch 40 316 316l stainless steel butt weld pipe manufacturers, suppliers, factory, SK85 JIS High Carbon Tool Steel, High Strength S690QL1 Steel, Wear Resistant Sheet NM360, X32 Carbon Steel Strip, Tool Steel, Wear NM400 Resistant Sheet