Stainless Steel Plate 316 Applications:
Chemical processing equipment
Pressure vessels
Pharmaceutical equipment
Heat exchangers
Food processing equipment
Marine applications
Oil and gas processing equipment

Send Inquiry

Product Introduction

316 Grades Stainless Steel Sheets with Different Surfaces

In conclusion, the choice of surface finish for 316 grades stainless steel sheets depends on the application. Each surface finish has its unique properties and benefits, making it suitable for specific industrial or decorative purposes.

2B Surface Finish - This is a smooth, reflective surface that is achieved by cold-rolling and annealing the steel sheet. The resulting finish is ideal for applications that require a clean, bright look, such as kitchen equipment, dairy equipment, and medical devices.

Brushed Finish - This finish is achieved by using abrasive belts to create a uniform, brushed appearance on the surface of the steel sheet. It is commonly used in architectural and industrial applications, where a unique, textured appearance is desired.

Mirror Finish - This is a highly reflective finish that produces a smooth, polished look similar to a mirror. It is commonly used in decorative applications, such as mirrors, furniture, and jewelry.

Satin Finish - This finish has a matte appearance and is achieved by using a series of abrasives until the desired level of reflectivity is achieved. It is commonly used in architectural applications, such as wall panels, elevator doors, and signage.

Chemistry Information: 316 Stainless Steel
Element	Percentage
C	0.08
Cr	18 max
Mn	2
Fe	82
Mo	3 max
Ni	14 max
P	0.045
S	0.03
Si	1

Mechanical Properties

		ASTM
	Typical*	Type 316	Type 316L
0.2% Offset Yield Strength, ksi	44	30 min.	25 min.
Ultimate Tensile Strength, ksi	85	75 min.	70 min.
Elongation in 2 inches, %	56	40 min.	40 min.
Reduction in Area, %	69	-	-
Hardness, Rockwell B	81	95 max.	95 max.