Mn13 Abrasion Resistant Steel Plates
Mn13 Abrasion Resistant Steel Plates
Mn13 Abrasion Resistant Steel Plates

Mn13 Abrasion Resistant Steel Plates

Brand: Mn13
C: 0.90-1.20
Si: 0.30-0.80
Mn: 11.00-14.00
P: ≤0.035

Send Inquiry

Product Introduction

MN13 is a high strength abrasion resistant steel plate manufactured by the Chinese company Baosteel. It has a nominal hardness of 450HBW, which makes it suitable for use in applications where high resistance to wear and abrasion is required. MN13 steel plates are widely used in industries such as mining, cement, construction, and heavy engineering. They offer superior toughness, impact resistance, and bendability, making them ideal for use in high-stress environments. MN13 steel plates are available in thicknesses ranging from 6mm to 60mm, and widths up to 2200mm. They can also be cut to size to meet specific customer requirements.

Sheet thickness range: 6mm-50mm
Surface state: ordinary surface and sandblasted surface
Size and shape: Custom cutting size and shape
Various processing: cutting, drilling, bending, welding and cutting can be performed
Wear resistance: mn13 steel plate has excellent wear resistance and corrosion resistance, and is an ideal material for the manufacture of wear resistant equipment and mechanical parts.
Application industry: mn13 steel plate is widely used in mining, construction, mining machinery, engineering machinery, civil engineering, port construction, metallurgical equipment, metallurgical machinery, power equipment, cement plant and grinding machinery and other fields.
Quality assurance: The mn13 steel plates we provide are 100% qualified, and each steel plate has undergone strict quality inspection and certification tests.
Advantages: mn13 steel plate has high hardness, high strength, high toughness and excellent wear resistance, which can meet various working conditions and requirements.
Manufacturer service: We provide perfect pre-sale consultation, sale service and after-sales support to ensure that customers get the best service and the most satisfactory products.
In summary, mn13 steel plate has a wide range of application prospects and market demand, can become your ideal choice.

Chemical Composition and Mechanical Properties(In Quenched & Tempered State):

Chemical Composition		Mechanical Properties(In Quenched & Tempered State)
C	0.90-1.20	Tensile strength(MPA)	≥800MPa
Si	0.30-0.80	Yield strength (MPA)	-----
Mn	11.00-14.00	Elongation(δ5/%)	≥40
P	≤0.035	Reduction in Area (ψ/%)	≥90
S	≤0.030	Hardness	>300