Mn13 Hot Rolling Plate
C: 0.90-1.20
Si: 0.30-0.80
Mn: 11.00-14.00
P: ≤0.035
Mn13 hot rolling plate
mn13 is high manganese steel, high manganese steel is a solid solution treatment, the temperature of solid solution treatment is 1050~1100 degrees, when heating, 650 degrees below the speed of 50~100 degrees /h heating, 650 degrees above the speed of 50~150 degrees /h heating, the best in 650~700 degrees of insulation 1~3h, holding time according to 25mm/h, Water cooling, water temperature does not exceed 20 degrees, quenched water temperature does not exceed 45 degrees.
Product Application Areas:
Our products have been used in all kinds of areas, such as aviation,aerospace,navigation,nuclear energy,chemical
industry,electronic information,achine manufacture, petrochemical, automotive,instrument and meter, Communication ,
transportation, and medical instruments, etc.
Product Sales Information:
|
Size |
Thickness:6mm-50mm Length:500mm-6000mm |
|
Origin place |
Made In China |
|
Delivery Condition |
Hot rolled,cold drawn,forged |
|
Surface require |
Black,grinding,bright,polish |
|
Heat treatment |
Quenched,Tempered,annealed |
|
Packing |
seaworthy packing ,wooden case ,carton,woven bag or at client's requires |
|
Delivery time |
In 10-50 days |
|
Trade Term |
EXW,FOB,CIF |
|
Payments |
T/T or L/C at sight |
|
Port |
China main Port,such as shanghai,Dalian,Shenzhen port. |
|
MOQ |
100kg |
Chemical Composition and Mechanical Properties(In Quenched & Tempered State):
|
Chemical Composition |
Mechanical Properties(In Quenched & Tempered State) |
||
|
C |
0.90-1.20 |
Tensile strength(MPA) |
≥800MPa |
|
Si |
0.30-0.80 |
Yield strength (MPA) |
----- |
|
Mn |
11.00-14.00 |
Elongation(δ5/%) |
≥40 |
|
P |
≤0.035 |
Reduction in Area (ψ/%) |
≥90 |
|
S |
≤0.030 |
Hardness |
>300 |
Quality Control
Product Uses
Hot Tags: mn13 hot rolling plate, China mn13 hot rolling plate manufacturers, suppliers, factory