Mn13 Wear Resistant Layer
Mn13 Wear Resistant Layer
Mn13 Wear Resistant Layer
Mn13 Wear Resistant Layer

Mn13 Wear Resistant Layer

Material: Mn13X120Mn12DIN1.3401
Thickness: 3mm-200mm
Width: 1000mm-3000mm
Length: 2000mm-12000mm
Surface treatment: hot rolling and cold rolling
Tensile strength: ≥685MPa
Yield strength: ≥430MPa
Elongation: ≥35%
Hardness: HB240-320

Send Inquiry

Product Introduction

Mn13 Wear resistant Layer

Name: Mn13 Wear resistant Layer (Mn13 Wear resistant layer)
Material: high manganese steel alloy
Characteristics: Good wear resistance, impact resistance, pressure resistance, long life.
Specifications: The thickness is generally 3-30mm, the width can reach more than 3000mm, and the length is customized according to customer needs.
Application field: Mainly used in construction machinery, mining machinery, coal mining machinery, cement machinery and other fields of wear-resistant parts manufacturing.
Advantages: Good wear resistance, can effectively reduce equipment maintenance costs and downtime, improve equipment use efficiency and production efficiency.
Precautions: Pay attention to the correct welding methods and skills during installation to avoid hot cracks and other problems. At the same time, pay attention to its regular inspection and maintenance.

Mechanical properties

Tensile Strength	Elongation	20°C Impact Resistance	Initial Hardness(HB)	Hardness after Hardened(HB)	180°old Bending Test
≥900MPa	≥40%	ak≥50(J)	190-250	≥300	Qualified