Wear Plate in Stock Nm360
Wear Plate in Stock Nm360
Wear Plate in Stock Nm360
Wear Plate in Stock Nm360

Wear Plate in Stock Nm360

Chemical composition of NM360 wear-resistant steel plate:
Carbon C content: 0.25;
Si content: 0.70;
Mn content: 1.60;
P content: 0.025;
Sulfur S content: 0.015;
Chromium Cr content: 0.80;
Nickel Ni content: 0.50;
Molybdenum Mo content: 0.50;
Ti content: 0.050;
Aluminum Als content: ≥0.010;

Send Inquiry

Product Introduction

Wear plate in stock nm360

NM360 wear-resistant plate is the common name of Nm360, which is a kind of alloy material with high hardness and strength. Because of its very high hardness, it can withstand very high pressure; At the same time, the strength of this material is particularly large, so it can be used in many special fields.

So, what are the characteristics of NM360 wear plate? Let's take a look at what the NM360 wear-resistant plate is made of.

1, NM360 excellent impact resistance: under the pressure of more than 500kgf/cm2, it can still maintain a high impact resistance

2, surface hardening layer: through the use of micro-refining process, the surface of the steel plate to form a hard metal oxide protective film. This not only improves the wear resistance of the steel plate, but also improves the oxidation resistance of the steel.

3, good machinability and weldability: steel plate can be hot rolled, forging and machining. Compared with the traditional quenching and tempering treatment of H13, it has higher hardness and better toughness. The sheet can be used in high-wear parts, gear and shaft parts, and high-strength mechanical parts.

4, good comprehensive mechanical properties: good toughness, good plastic deformation effect, and has good welding and riveting performance. In addition, due to the high yield point and strength of the material, it has good creep resistance and low notch sensitivity at high temperatures.

5, excellent low temperature compressive resistance, bending resistance and lasting strength. For the operating temperature range from -40°C to +120°C, there is a high fatigue limit and fracture toughness. In addition, it has good cold forming performance and low notch sensitivity.

6, excellent bending processing performance. The steel plate is easy to be cold and hot formed, and can be cut, bent, rolled, etc.

7, good corrosion resistance and oxidation resistance. Due to the carbon contained in the steel plate, it has a certain chemical stability; Coupled with the addition of chromium, it enhances its antioxidant function, so that it can work in harsh environments.

8, excellent corrosion resistance. When steel is exposed to acidic media (such as sulfuric acid or hydrochloric acid), neutral salt solutions or water (sea water), erosion will quickly occur, resulting in destruction. However, the use of containers made of aluminum-containing manganese alloy, even under the above conditions will not occur any corrosion phenomenon. This is because the aluminum ions in the aluminum-manganese alloy combine with chloride ions to form a dense oxide film, which prevents the dissolution of the medium to the steel matrix.

9, low friction coefficient. Because of the special high-quality ferrite structure, the friction coefficient of this new composite material is very low, only 0.07 ~ 0.1. This can effectively reduce the degree of equipment wear.