STAINLESS STEEL 316L PIPE Mechanical property
Tensile strength σb (MPa) : ≥480
Conditional yield strength σ0.2 (MPa) : ≥177
Elongation δ5 (%) : ≥40
Section shrinkage ratio ψ (%) : ≥60
Hardness: ≤187HB; ≤90HRB; ≤200HV
Density: 7.98g/cm3;
Specific heat capacity ratio (20℃) : 0.502J/(g*K)

Send Inquiry

Product Introduction

STAINLESS STEEL 316L PIPE Ø 28 LENGTH 6M

The Mo content of 316L makes the steel has excellent pitting resistance and can be safely used in halogen ion environments such as Cl-. Because 316L is mainly used for its chemical properties, steel mills have slightly lower surface inspection requirements for 316L (relative to 304), and customers with higher surface requirements should strengthen surface inspection efforts.

Stainless Steel 316L Pipe Chemical Composition

Grade		C	Mn	Si	P	S	Cr	Mo	Ni	N
316	Min	-	-	-	0	-	16.0	2.00	10.0	-
316	Max	0.08	2.0	0.75	0.045	0.03	18.0	3.00	14.0	0.10
316L	Min	-	-	-	-	-	16.0	2.00	10.0	-
316L	Max	0.03	2.0	0.75	0.045	0.03	18.0	3.00	14.0	0.10

ASTM A312 TP 316L Pipes Mechanical Properties

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elong (% in 50mm) min	Hardness
Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elong (% in 50mm) min	Rockwell B (HR B) max	Brinell (HB) max
316	515	205	40	95	217
316L	485	170	40	95	217

Stainless Steel UNS S31603 Pipes Equivalent Grades

Grade	UNS No	Old British		Euronorm		Swedish SS	Japanese JIS
Grade	UNS No	BS	En	No	Name	Swedish SS	Japanese JIS
316	S31600	316S31	58H, 58J	1.4401	X5CrNiMo17-12-2	2347	SUS 316
316L	S31603	316S11	-	1.4404	X2CrNiMo17-12-2	2348	SUS 316L