Stainless Steel Welded Pipe Type 316L

Stainless Steel Welded Pipe Type 316L

Most of the existing 316l on the market are produced in accordance with the American standard. For cost considerations, steel mills generally put the ni content of products as close to the lower limit as possible. The American standard stipulates that the ni content of 316l is 10 ~ 14%, and the Japanese standard stipulates that the ni content of 316l is 12 ~ 15%. According to the minimum standard, there is a 2% difference between the American standard and the Japanese standard in the ni content, which is still quite huge in the price, so customers need to see clearly when purchasing 316l products, and the product is referred to astm (American standard) or jis (Japanese standard) standards.
Such as: 316l(US standard)
sus316l (Day mark)

Stainless Steel 316L Pipe Chemical Composition

 

Typical Chemical Composition % (maximum values, unless noted)

Weight %	C	Mn	P	S	Si	Cr	Ni	Mo
SS 316 Pipe	.08	2.00	.045	.030	1.00	16.0-18.0	11.0-14.0	2.0-3.0
SS 316L Pipe	.035	2.00	.045	.030	1.00	16.0-18.0	10.0-14.0	2.0-3.0

316L Stainless Steel Pipe Mechanical Properties

 

Grade	Tensile Strength
	Ultimate /Min		Yield Strength/ Min		Elongation/Min
	KSI	MPA	KSI	MPA	%
SS 316 Pipe	75	515	30	205	35
SS 316L Pipe	70	485	25	170	35

SS 316L Seamless Pipe Equivalent Grade

 

Grade	UNS No	Old British		Euronorm / EN		Swedish SS	Japan JIS
		BS	En	No	Name
316L	S31603	304S11	58E	1.4436	X3CrNiMo17-13-3	2348	SUS 316L

Application

Packing & Delivery

SURFACE

Product Testing

Hot Tags: stainless steel welded pipe type 316l, China stainless steel welded pipe type 316l manufacturers, suppliers, factory, High Carbon Steel Saw Blade, 50CrV4 Spring Alloy Steel Strip, 45Mn Carbon Steel Round Bar, 65Mn Spring Steel Round Bar, Wear Resistant Steel Plate, Wear NM400 Resistant Sheet