Material: 316 stainless steel
Surface treatment: 2B
Relative density: 7.98
Tensile strength: ≥520MPa
Yield strength: ≥205MPa
Elongation: ≥40%
Hardness: ≤187HBW

Send Inquiry

Product Introduction

Stainless Steel Plate AISI 316 is a high-grade stainless steel plate with excellent resistance to corrosion, staining, and rust. It has a molybdenum content of 2-3% that provides resistance to pitting and crevice corrosion in chloride environments. AISI 316 is a more corrosion-resistant type of stainless steel than AISI 304, making it suitable for use in harsh environments where exposure to corrosive chemicals, acids, or salty water is common. Also, it has good heat resistance for use in high-temperature applications. AISI 316 is typically used in industries like chemical, food processing, pharmaceuticals, and marine, among others.

Material: It is a high-quality stainless steel material, made of chromium, nickel and molybdenum.
Surface treatment: The surface can be polished, brushed sand, pickling and other treatments to obtain different appearance effects.
Size: The size can be customized according to customer requirements, common sizes are 1000mm * 2000mm, 1219mm * 2438mm, 1500mm * 6000mm and so on.
Thickness: The thickness is usually between 0.3mm and 100mm, which can be adjusted according to customer needs.
Uses: Widely used in chemical, petroleum, offshore engineering, construction, food processing and other fields, as well as the manufacture of ships, automobiles, aviation and train parts

Chemical Composition

Grade	C	Mn	Si	P	S	Cr	Mo	Ni	N
SS 316	0.08 max	2 max	1.0 max	0.045 max	0.030 max	16.00 – 18.00	2.00 – 3.00	11.00 – 14.00	67.845 min
SS 316L	0.035 max	2 max	1.00 max	0.045 max	0.030 max	16.00 – 18.00	2.00 – 3.00	10.00 – 14.00	68.89 min

Mechanical Properties

Grade	Density	Melting Point	Tensile Strength	Yield Strength (0.2%Offset)	Elongation
SS 316	8.0 g/cm3	1400 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35 %
SS 316L	8.0 g/cm3	1399 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35 %

Equivalent Grades

STANDARD	WERKSTOFF NR.	UNS	JIS	BS	GOST	AFNOR	EN
SS 316	1.4401 / 1.4436	S31600	SUS 316	316S31 / 316S33	–	Z7CND17‐11‐02	X5CrNiMo17-12-2 / X3CrNiMo17-13-3
SS 316L	1.4404 / 1.4435	S31603	SUS 316L	316S11 / 316S13	03Ch17N14M3 / 03Ch17N14M2	Z3CND17‐11‐02 / Z3CND18‐14‐03	X2CrNiMo17-12-2 / X2CrNiMo18-14-3