Abrasion Resistance Steel Wear Plates Nm360
Carbon C content: 0.25;
Si content: 0.70;
Mn content: 1.60;
P content: 0.025;
Sulfur S content: 0.015;
Chromium Cr content: 0.80;
Nickel Ni content: 0.50;
Molybdenum Mo content: 0.50;
Ti content: 0.050;
Aluminum Als content: ≥0.010;
Abrasion Resistance Steel Wear Plates Nm360
nm360 wear-resistant plate is a high-performance engineering plastic, mainly used in the manufacture of mechanical parts, especially in mechanical processing has excellent wear resistance.
The main feature of nm360 wear-resistant plate is that it has extremely high hardness and wear resistance, and its hardness can reach HRC68-70, which is equivalent to high-hardness metal, and can withstand wear and friction under harsh conditions such as high-speed, high temperature, high pressure, so it is widely used in machinery manufacturing, automotive, aerospace, energy, electronics, medical and other fields.
Chemical Composition (%) of NM360 Wear Resistant Steel
| C | Si | Mn | P | S | Cr | Mo | Ni | B |
| ≤0.17 | ≤0.50 | ≤1.5 | ≤0.025 | ≤0.015 | ≤0.70 | ≤0.40 | ≤0.50 | ≤0.005 |
Mechanical Properties of NM360 Wear Resistant Steel
| Thickness/mm | ReL /MPa | Rm /MPa | A/% | Hardness HBW10/3000 | Impact -20℃/J |
| 20 | 1050 | 1160 | 19.0 | 360.0 | 65 |
| 25 | 1020 | 1180 | 18.5 | 375.0 | 52 |
| 30 | 1040 | 1180 | 17.0 | 369.0 | 65 |
| 40 | 1020 | 1160 | 18.0 | 368.0 | 68 |
Contrast Test of Wear Resistance
| Test Group | Grade | Wear Test |
| A | WZB-NM360 | 1.16 |
| EEMS10104 (Sweden) | 1.00 | |
| B | WZB-NM400 | 1.21 |
| NK-EH400 (Japan) |
1.00 |
Product Application
Production Process
Hot Tags: abrasion resistance steel wear plates nm360, China abrasion resistance steel wear plates nm360 manufacturers, suppliers, factory, Wear Resistant Steel Plate, NM300 Wear Resistant Steel Sheet, Wear Resistant Sheet NM360, NM500 Resistant Steel Wear Plate, NM650 Wear Resistant Steel Plate, NM450 Wear Resistant Sheet