Wear-resistant plate is a kind of plate with good wear-resistant properties, which is widely used in the industrial field where it is necessary to resist wear. Its main role is to protect the surface of equipment or machinery from wear and damage

Send Inquiry

Product Introduction

Abrasion Resistant Plates

Wear-resistant steel plate is widely used in the industrial field of steel plate materials, according to wear resistance, manufacturing process, material and use can be divided into a variety of types. Different types of wear-resistant steel plates have different characteristics and scope of application, and the selection needs to be determined according to the specific use environment and wear-resistant requirements.

Classified by manufacturing process

1. Hot rolled wear-resistant steel plate: The wear-resistant steel plate produced by hot rolling process has the characteristics of rough surface, large thickness and high strength, and is suitable for heavy load and high impact conditions.
2. Cold rolled wear-resistant steel plate: wear-resistant steel plate produced by cold rolling process has the characteristics of smooth surface, thin thickness and high precision, which is suitable for some occasions with high wear-resistant performance requirements.
3. Cast wear-resistant steel plate: The wear-resistant steel plate produced by the casting process has the characteristics of dense organization and stable wear resistance, which is suitable for some special wear conditions.

Classification by use

1. Mine wear-resistant steel plate: suitable for mining machinery, mining equipment, excavators and other equipment wear-resistant plate, with high strength, high wear resistance and other characteristics.
2. Metallurgical wear-resistant steel plate: suitable for metallurgical equipment, such as blast furnace, converter, continuous casting machine and other equipment wear-resistant plate, required to have high temperature resistance, oxidation resistance, corrosion resistance and other characteristics.
3. Cement wear-resistant steel plate: suitable for cement production equipment wear-resistant plate, such as cement mill, cement conveying equipment, etc., requiring wear resistance, impact resistance, corrosion resistance and other characteristics.
4. Construction wear-resistant steel plate: suitable for construction sites, such as wear-resistant floor, wear-resistant stairs, etc., requiring non-slip, wear-resistant, easy to clean and other characteristics.

Welding properties of common wear plates

FAST DELIVERY NM360 NM400 NM450 NM5000 HIGHT QUALITY MS WEAR RESISTANT STEEL PLATE IN STOCK

XAR 500 XAR 400 Abrasion Resistant Steel Plate

Fast delivery Wear Resistant Steel Plate

Corrosion resistant steel plate Sheet NM500 WNM500

Main Grade

Material

DIN: XAR300,XAR400, XAR450, XAR500, XAR600, DILLIDUR400V,DILLIDUR450V,DILLIDUR500V; X120Mn12; 1.3401;

SSAB:400,450,500,550,600;WELDX700,WELDX900,WELDX960;

NF: FORA400,FORA500,Creusabro4800,Creusabro8000;

EN: QUARD400,QUARD450,QUARD500 ; RAEX320,RAEX400,RAEX450,RAEX500;
DUrostat400,DUrostat450,DUrostat500;

JIS: JFE-EH360,JFE-EH400,JFE-EH500, WEL-HARD400, WEL-HARD500; SUMIHARD-K340,SUMIHARD-K400,SUMIHARD-K500

GB: NM360,NM400,M450,NM500,NM550,NM600,NR360,NR400,B-HARD360,B-HARD400,B-HARD450,KN-55,KN-60,KN-63.

Thickness,Width,Length:
Thickness:common 2~100 mm (1~300 mm)
Width:common 1000~2200 mm (600~2500 mm)
Length:1000~12000 mm

Chemical Composition
Grade	Chemical Composition / %
	C	Si	Mn	P	S	Cr	Ni	Mo	Ti	B	Als
	≤ Not More Than									Range	≥
NM300	0.23	0.70	1.60	0.025	0.015	0.70	0.50	0.40	0.050	0.0005~0.006	0.010
NM360	0.25	0.70	1.60	0.025	0.015	0.80	0.50	0.50	0.050	0.0005~0.006	0.010
NM400	0.30	0.70	1.60	0.025	0.010	1.00	0.70	0.50	0.050	0.0005~0.006	0.010
NM450	0.35	0.70	1.70	0.025	0.010	1.10	0.80	0.55	0.050	0.0005~0.006	0.010
NM500	0.38	0.70	1.70	0.020	0.010	1.20	1.00	0.65	0.050	0.0005~0.006	0.010
NM550	0.38	0.70	1.70	0.020	0.010	1.20	1.00	0.70	0.050	0.0005~0.006	0.010
NM600	0.45	0.70	1.90	0.020	0.010	1.20	1.00	0.80	0.050	0.0005~0.006	0.010

Mechanical Property
Grade	Thickness mm	Tensile Strength R_m / Mpa	Elongation A_50mm / %	Impact Energy KV₂ / J	Brinell Hardness HBW
NM300	≤80	≥1000	≥14	≥24	270-330
NM360	≤80	≥1100	≥12	≥25	330-390
NM400	≤80	≥1200	≥10	≥26	370-430
NM450	≤80	≥1250	≥7	≥27	420-480
NM500	≤70	-	-	-	≥470
NM550	≤70	-	-	-	≥530
NM600	≤60	-	-	-	≥570