Mn13 High Manganese Hot Rolled Wear Resistant Steel Plate Sheet

Mn13 High Manganese Hot Rolled Wear Resistant Steel Plate Sheet
Mn13 High Manganese Hot Rolled Wear Resistant Steel Plate Sheet
Mn13 High Manganese Hot Rolled Wear Resistant Steel Plate Sheet
Mn13 High Manganese Hot Rolled Wear Resistant Steel Plate Sheet

Mn13 High Manganese Hot Rolled Wear Resistant Steel Plate Sheet

Material: Mn13X120Mn12DIN1.3401
Thickness: 3mm-200mm
Width: 1000mm-3000mm
Length: 2000mm-12000mm
Surface treatment: hot rolling and cold rolling
Tensile strength: ≥685MPa
Yield strength: ≥430MPa
Elongation: ≥35%
Hardness: HB240-320

Send Inquiry

Product Introduction

The following are the main specifications of Mn13 high manganese hot rolled wear-resistant steel plate:

1. Plate thickness: 6-50mm

2. Plate width: 1500-2700mm

3. Board length: 6000-12000mm

4. Surface state: conventional surface treatment or customized according to customer requirements

Mn13 high manganese hot rolled wear-resistant steel plate has very high wear resistance and excellent toughness and strength. It can be used in the manufacture of mining machinery, engineering machinery, casting parts, wear parts and other high-wear areas of parts. In addition, this steel plate can also be used in a variety of machinery manufacturing, pressure vessels and shipbuilding and other fields.

The application of Mn13 high manganese hot rolled wear-resistant steel plate can improve the wear resistance of parts, extend the service life and reduce the maintenance cost. At the same time, the production and sale of this steel plate has also stimulated the technological progress and economic development of related industries.

Chemical composition(%)

Brand	C	Si	Mn	P	S
X120Mn12/Mn13	0.90-1.20	0.30-0.80	11.00-14.00	≤0.035	≤0.030

Mechanical Properties

Tensile Strength	Elongation	20°C Impact Resistance	Initial Hardness(HB)	Hardness after Hardened(HB)	180°old Bending Test
≥900MPa	≥40%	ak≥50(J)	190-250	≥300	Qualified