Material: Mn13X120Mn12DIN1.3401
Thickness: 3mm-200mm
Width: 1000mm-3000mm
Length: 2000mm-12000mm
Surface treatment: hot rolling and cold rolling
Tensile strength: ≥685MPa
Yield strength: ≥430MPa
Elongation: ≥35%
Hardness: HB240-320

Send Inquiry

Product Introduction

x120mn12 steel plate MN13 steel plate 1.3401

Characteristics of products

·High abrasive resistance

·Strong plasticity and impact toughness

·It is work hardening steel - the more impact and abrasion it gets the harder the surface becomes.

·Steel stays ductile underneath - only surface layer hardens.

·With continued impact steel can harden to 500HB above.

·When rolled - never brittle.

·Low friction properties.

·Non-magnetic.
Wear Resistant Manganese steel plate ASTM A128 Mn13 X120Mn12 K700

Wear Resistant Steel Plate Chemical Composition and Mechanical Properties
Chemical Composition(Max)
Material		C			Si	Mn			P			S			Cr		Ni			Mo	Ti			Bt			Als	CEV
NM300		0.23			0.70	1.60			0.025			0.015			0.70		0.50			0.40	0.050			0.0005-0.0006			0.010	0.45
NM360		0.25			0.70	1.60			0.025			0.015			0.80		0.50			0.50	0.050			0.0005-0.0006			0.010	0.48
NM400		0.30			0.70	1.60			0.025			0.010			1.00		0.70			0.50	0.050			0.0005-0.0006			0.010	0.55
NM450		0.35			0.70	1.70			0.025			0.010			1.10		0.80			0.55	0.050			0.0005-0.0006			0.010	0.60
NM500		0.38			0.70	1.70			0.020			0.010			1.20		1.00			0.65	0.050			0.0005-0.0006			0.010	0.65
NM550		0.38			0.70	1.70			0.020			0.010			1.20		1.00			0.70	0.050			0.0005-0.0006			0.010	0.72
NM600		0.38			0.70	1.90			0.020			0.010			1.50		1.00			0.70	0.050			0.0005-0.0006			0.010	0.76
Material							Tensile MPA						Elongation %								Impact energy -20ºC						HBW
NM300							≥1000						≥14								≥24						270-300
NM360							≥1100						≥12								≥24						330-390
NM400							≥1200						≥10								≥24						370-430
NM450							≥1250						≥7								≥24						420-480
NM500							≥1250						≥7								≥24						≥470
NM550							≥1250						≥7								≥24						≥530
NM600							≥1250						≥7								≥24						≥570
Grade	C			Si			Mn			P			S			Cr			Mo				Cu		Ni		B
XAR400	0.20			0.80			1.50			0.025			0.010			1.00			0.50				--		--		0.005
XAR450	0.22			0.80			1.50			0.025			0.012			1.30			0.50				0.30		--		0.005
XAR500	0.28			0.80			1.50			0.025			0.010			1.00			0.50				--		--		0.005
XAR600	0.40			0.80			1.50			0.025			0.010			1.50			0.50				--		1.50		0.005
Grade	Yield Strength Reh MPa										Tensile Strength Rm MPa							Elongation								BH (Brinell Hardness)
XAR400	1150										1300							≥12								360-440
XAR450	1200										1350							≥10								410-490
XAR500	1500										1600							≥9								450-530
XAR600	--										--							--								≥550
Material			C					Si						Mn				P				S				Cr
Mn13			1.1~1.3					0.3~0.5						12~13				≤0.100				≤0.040				≤1.5
X120Mn12			1.1~1.3					0.3~0.5						12~13				≤0.100				≤0.040				≤1.5
1.3401			1.1~1.3					0.3~0.5						12~13				≤0.100				≤0.040				≤1.5
SCMnH11			0.9~1.5					0.3~1.0						10~15				≤0.100				≤0.050				≤1.5
ASTM A128			1.1~1.3					0.3~0.5						12~13				≤0.100				≤0.050				≤1.5