Chemical composition of NM360 wear-resistant steel plate:
Carbon C content: 0.25;
Si content: 0.70;
Mn content: 1.60;
P content: 0.025;
Sulfur S content: 0.015;
Chromium Cr content: 0.80;
Nickel Ni content: 0.50;
Molybdenum Mo content: 0.50;
Ti content: 0.050;
Aluminum Als content: ≥0.010;

Send Inquiry

Product Introduction

Nm360 is a high-strength wear-resistant steel plate. It has a Brinell hardness of 360 HBW and a thickness range of 6 to 80mm. The 8mm thick Nm360 steel plate is commonly used in industries that require high wear resistance, such as mining, construction, and cement plants. Due to its excellent mechanical properties, Nm360 steel plate is resistant to wear, impact, and corrosion. It can withstand harsh working conditions and is long-lasting. The steel plate is also easy to weld and cut, making it relatively easy to process. In conclusion, Nm360 8mm thick steel plate is a high-performance wear-resistant steel plate that is widely used in various industries. Its excellent properties make it ideal for harsh working conditions and heavy machinery.

Wear/Abrasion Resistant Steel Equivalent Standards

Steel Grade	JFE	DILLIDUR	ThyssenkKrupp	Ruukki
NM360	EH360	-	-	-
NM400	EH400	400V	XAR400	Raex400
NM450	-	450V	XAR450	Raex450
NM500	EH500	500V	XAR500	Raex500

Chemical Composition (%) of NM Wear Resistant Steel

Steel Grade	C	Si	Mn	P	S	Cr	Mo	B	N	H	Ceq
NM360/NM400	≤0.20	≤0.40	≤1.50	≤0.012	≤0.005	≤0.35	≤0.30	≤0.002	≤0.005	≤0.00025	≤0.53
NM450	≤0.22	≤0.60	≤1.50	≤0.012	≤0.005	≤0.80	≤0.30	≤0.002	≤0.005	≤0.00025	≤0.62
NM500	≤0.30	≤0.60	≤1.00	≤0.012	≤0.002	≤1.00	≤0.30	≤0.002	≤0.005	≤0.0002	≤0.65
NM550	≤0.35	≤0.40	≤1.20	≤0.010	≤0.002	≤1.00	≤0.30	≤0.002	≤0.0045	≤0.0002	≤0.72

Mechanical Properties of NM Wear Resistant Steel

Steel Grade	Yield Strength /MPa	Tensile Strength /MPa	Elongation A50 /%	Hardess (Brinell) HBW10/3000	Impact/J （-20℃）
NM360	≥900	≥1050	≥12	320-390	≥21
NM400	≥950	≥1200	≥12	380-430	≥21
NM450	≥1050	≥1250	≥7	420-480	≥21
NM500	≥1100	≥1350	≥6	≥470	≥17
NM550	-	-	-	≥530	-

Abrasion Resistant Steel Plate Availabillity

Grade	Thickness	Width	Length
AR200 / AR 235	3/16" – 3/4"	48" – 120"	96" – 480"
AR400F	3/16" – 4"	48" – 120"	96" – 480"
AR450F	3/16" – 2 "	48" – 96 "	96" – 480"
AR500	3/16" – 2 "	48" – 96 "	96" – 480"
AR600	3/16" – 3/4"	48" – 96 "	96" – 480"

Chemical Composition of Abrasion Resistant Steel Plate

Grade	C	Si	Mn	P	S	Cr	Ni	Mo	B
AR500	0.30	0.7	1.70	0.025	0.015	1.00	0.70	0.50	0.005
AR450	0.26	0.7	1.70	0.025	0.015	1.00	0.70	0.50	0.005
AR400	0.25	0.7	1.70	0.025	0.015	1.50	0.70	0.50	0.005
AR300	0.18	0.7	1.70	0.025	0.015	1.50	0.40	0.50	0.005

Mechanical Properties of Abrasion Resistant Steel Plate

Grade	Yield Strength MPa	Tensile Strength MPa	Elongation A	Impact Strength Charpy V 20J	Hardness Range
AR500	1250	1450	8	-30C	450-540
AR450	1200	1450	8	-40C	420-500
AR400	1000	1250	10	-40C	360-480
AR300	900	1000	11	-40C	-