NM400 Chemical composition
C 0.25 or less
Si 0.70 or less
Mn 1.60 or less
P 0.025 or less
S 0.010 or less
Cr 1.4 or less
Mo 0.50 or less
Ni 1.00 or less
B 0.004 or less

Send Inquiry

Product Introduction

Nm400 Abrasion Wear Resisitant Steel Plate Ar400 Sheet

Flame cutting should follow the following minimum preheating temperature: plate thickness 30~50mm, 75°C (170°F); Plate thickness 50~100mm, 100°C (212°F); Plate thickness more than 100mm, 150°C (302°F).

machining

400V machining can use high-speed steel bits, especially cobalt alloy high-speed bits. If the proper penetration rate and penetration rate are used, the bit can achieve satisfactory service life.

General technical delivery requirements

Unless otherwise agreed, general delivery techniques require the use of EN 10021.

Application examples: earthmoving machinery, loading machinery, dredger, tipping mine car, conveying equipment, dump truck, shredder blade, waste treatment and recycling equipment, etc.

item	value
Standard	AiSi, ASTM, bs, DIN, GB, JIS
Place of Origin	China
Type	Steel Plate
Technique	Hot Rolled
Surface Treatment	Coated
Width	600mm-2500mm Or custom
Length	as customer required
Tolerance	±1%
Type	Cold Rolled Steel Sheet
Processing Service	Bending, Welding, Decoiling, Cutting, Punching
Delivery Time	2-7 Days
Product Name	Carbon Steel Plate