NM450 Wear-resistant Steel
Yield strength Re (MPa) : 1000
Tensile strength Rm (MPa) : 1250
Elongation A5:10
Test temperature: 20 (20F)
Impact power Charpy-V longitudinal (J) : 45
Hardness: HBW420-480
NM450 wear-resistant steel
NM450 steel is usually manufactured using the hot rolling process to obtain high production efficiency and stable product quality. Because compared with other processing processes such as forging and casting, hot rolling process has the following advantages: 1, high production efficiency: hot rolling process is suitable for mass production, and can be quickly processed into steel plates that meet the standard size. 2, quality stability: hot rolling process can control raw material temperature and processing parameters to ensure the stability of product quality. 3, low cost: hot rolling process does not require special molding equipment and technology, the cost is relatively low.
|
roduct Name |
Wear Resistant Steel Plate |
|
Shape |
Steel Sheet |
|
Standard |
ASTM, JIS, EN, GB |
|
Material |
NM300, NM360, NM400, NM450, NM500, NM550, NM600 |
|
Width |
Customize |
|
Length |
Customize |
|
Thickness |
3-300mm |
|
Thickness Classification |
Thin plate, Medium plate, Thick plate, Extra thick plate |
|
Application |
Bridges, boilers, shipbuilding, armor, automobiles, roofing and so on. |
Productive Process
Product Application:
Quality test
Hot Tags: nm450 wear-resistant steel, China nm450 wear-resistant steel manufacturers, suppliers, factory, NM650 Wear Resistant Steel Plate, Wear Resistant Sheet NM360, NM450 Wear Resistant Sheet, NM300 Wear Resistant Steel Sheet, Wear NM400 Resistant Sheet, Wear Resistant Steel Plate