1.0601, DIN C60, AISI 1060 Steel
1. Product specifications:
- Material standard: 1.0601 / DIN C60 / AISI 1060
- Chemical composition: Carbon C: 0.57-0.65%; Silicon Si: 0.15-0.35%; Manganese Mn: 0.6-0.9%; P: max. 0.025%; Sulfur S: max. 0.035%
- Mechanical properties: yield strength ≥620 MPa; Tensile strength ≥730 MPa; Elongation ≥12%
2. These product specifications show that 1.0601, DIN C60 and AISI 1060 steel are high quality industrial materials. Their chemical composition and mechanical properties are carefully formulated and optimized to meet a wide range of industrial needs.
3. 1.0601, DIN C60 and AISI 1060 steels are used in a wide range of applications: from simple construction to the manufacture of heavy machinery to the manufacture of automobiles and aircraft.
4. In industrial applications, the advantages of 1.0601, DIN C60 and AISI 1060 steels lie in their strength and durability. They can withstand extreme stresses and pressures while being exceptionally ductile and malleable.
| Cr + Mo + Ni = max 0.63 |
| C | Si | Mn | Ni | P | S | Cr | Mo |
| 0.57 - 0.65 | max 0.4 | 0.6 - 0.9 | max 0.4 | max 0.045 | max 0.045 | max 0.4 | max 0.1 |
MECHANICAL PROPERTIES:
| Effect of the cross-section on mechanical properties | |||
| If heat treated | |||
| Diameter d, mm
Thickness of the flat bar t, mm |
≤ 16
≤ 8 |
16 – 40
8 – 20 |
40 – 100
20 – 60 |
| Ultimate tensile strength, Rm, MPa | 850 – 1000 | 800 – 950 | 750 – 900 |
| Yield stress Re (Rp0.2), MPa | ≥ 580 | ≥ 520 | ≥ 450 |
| Elongation, A, % | ≥ 11 | ≥ 13 | ≥ 14 |
| Reduction of area, Z, % | ≥ 25 | ≥ 30 | ≥ 35 |
| If normalised | |||
| Diameter, d, mm
Thickness of the flat bar t, mm |
≤ 16
≤ 16 |
16 – 100
16 – 100 |
100 – 250
100 – 250 |
| Ultimate tensile strength, Rm, MPa | ≥ 710 | ≥ 670 | ≥ 650 |
| Yield stress Re (Rp0.2), MPa | ≥ 380 | ≥ 340 | ≥ 310 |
| Elongation, A, % | ≥ 10 | ≥ 11 | ≥ 11 |
TECHNOLOGICAL TREATMENT PROCESSES:
| Technological treatment processes | Possible application | Temperature, °C | ||
| Hot forming | Forging | + | (1050 – 850) | |
| Rolling | + | (1050 – 850) | ||
| Treatment | Heat treatment | Quenching | + | 810-850/w,o |
| Tempering | + | 550 – 660 | ||
| Precipitation strengthening | Supersaturation | – | – | |
| Ageing | – | – | ||
| Annealing | Normalising | + | 820 – 880 | |
| Soft annealing | + | (650 – 700) | ||
| Thermochemical treatment | Carburising | – | – | |
| Other | – | – | ||
TECHNOLOGICAL TREATMENT PROCESSES:
| Technological treatment processes | Possible application | Temperature, °C | ||
| Hot forming | Forging | + | (1050 – 850) | |
| Rolling | + | (1050 – 850) | ||
| Treatment | Heat treatment | Quenching | + | 810-850/w,o |
| Tempering | + | 550 – 660 | ||
| Precipitation strengthening | Supersaturation | – | – | |
| Ageing | – | – | ||
| Annealing | Normalising | + | 820 – 880 | |
| Soft annealing | + | (650 – 700) | ||
| Thermochemical treatment | Carburising | – | – | |
| Other | – | – | ||
Inspection:
Product Application
Hot Tags: 1.0601, din c60, aisi 1060 steel, China 1.0601, din c60, aisi 1060 steel manufacturers, suppliers, factory, Cold Rolled High Carbon Steel Coil, 65Mn Spring Steel Round Bar, Cold Drawn Steel Round Bar, Calibrate Steel Rod, S20C Carbon Steel, Carbon Steel Round Bar C60
Previous