The wear resistance of Mn13 rolled steel plate is very good in the environment of strong impact and high pressure.

Send Inquiry

Product Introduction

High Manganese Steel Mn13

Its chemical composition is (%) :

C0.90 ~ 1.50

Mn10.0 to 15.0

Si0.30 ~ 1.0

S 0.05 or less

P 0.10 or less

Scope of application

With high tensile strength, plasticity and toughness and non-magnetic, even if the parts wear to very thin, still can withstand the larger impact load without breaking, can be used for casting a variety of impact-resistant wear parts, such as ball mill liner, excavator bucket teeth, crusher teeth and so on. It is generally used for low-impact castings with simple structure and wear resistance, such as lining plate, tooth plate, crushing wall, rolling wall, roll sleeve and shovel teeth.

Application	Widely used in a variety of architectural and engineering structures,such as 1.) metal constructions such as buildings,bridges,ships; 2.) transmission tower, reaction tower; 3.) lifting transportation machinery; 4.) industrial furnace;boilers 5.) container frame, warehouse goods shelves, etc
Certificate	MTC will be provided with goods, third part inspection is acceptable, for example BV,SGS.
Standard grade	DIN: XAR300,XAR400, XAR450, XAR500, XAR600, DILLIDUR400V,DILLIDUR450V,DILLIDUR500V; X120Mn12; 1.3401; SSAB:400,450,500,550,600;WELDOX700,WELDOX900,WELDOX960; NF: FORA400,FORA500,Creusabro4800,Creusabro8000; EN: QUARD400,QUARD450,QUARD500 ; RAEX320,RAEX400,RAEX450,RAEX500; DUrostat400,DUrostat450,DUrostat500; JIS: JFE-EH360,JFE-EH400,JFE-EH500, WEL-HARD400, WEL-HARD500; SUMIHARD-K340,SUMIHARD-K400,SUMIHARD-K500 GB: NM360,NM400,M450,NM500,NM550,NM600,NR360,NR400,B-HARD360,B-HARD400,B-HARD450,KN-55,KN-60,KN-63.
Trading term	EXW, FOB, CFR, CIF