Mn13 X120Mn12 Steel Plate
Mn13 X120Mn12 Steel Plate
Mn13 X120Mn12 Steel Plate
Mn13 X120Mn12 Steel Plate

Mn13 X120Mn12 Steel Plate

Material: Mn13X120Mn12DIN1.3401
Thickness: 3mm-200mm
Width: 1000mm-3000mm
Length: 2000mm-12000mm
Surface treatment: hot rolling and cold rolling
Tensile strength: ≥685MPa
Yield strength: ≥430MPa
Elongation: ≥35%
Hardness: HB240-320

Send Inquiry

Product Introduction

Mn13 and X120Mn12 are both types of high manganese steel plate, also known as Hadfield steel. These plates are highly wear-resistant and have excellent impact resistance, making them suitable for use in a variety of applications where abrasion and impact are common, such as in mining, construction, and engineering.

Mn13 and X120Mn12 steel plates have a manganese content of 11-14%, which is significantly higher than standard carbon steel (usually around 0.25%). This high level of manganese makes the steel extremely hard and durable, and also helps to improve its toughness and resistance to cracking and deformation under stress.

Both Mn13 and X120Mn12 steel plates are often used in applications where heavy wear and tear is expected, such as in crushers, conveyor belts, and earthmoving equipment. They are also used in parts like excavator buckets, shovel teeth, and other mining and construction equipment.

Thickness: 6-40mm
Width: 1500-2500mm
Length: 3000-12000mm
Surface treatment: polishing, shot blasting, spinning
Application: excavators, loaders, mining machinery, cement equipment, concrete mixing equipment, etc.

Mechanical properties

Tensile Strength	Elongation	20°C Impact Resistance	Initial Hardness(HB)	Hardness after Hardened(HB)	180°old Bending Test
≥900MPa	≥40%	ak≥50(J)	190-250	≥300	Qualified