Din 1.3401 K700 Mn13 X120Mn12 High Manganese Steel Plate
Thickness: 3mm-200mm
Width: 1000mm-3000mm
Length: 2000mm-12000mm
Surface treatment: hot rolling and cold rolling
Tensile strength: ≥685MPa
Yield strength: ≥430MPa
Elongation: ≥35%
Hardness: HB240-320
The Din 1.3401 K700 Mn13 X120Mn12 High Manganese steel plate is an ideal material for applications that require high strength, toughness, and resistance to abrasion and wear, particularly in harsh environments.
The high-manganese steel plate is a steel with extremely high wear resistance and impact resistance, making it one of the best materials for the manufacture of wear-resistant parts. It has excellent mechanical properties, extremely high tensile strength and yield strength, and also has very good plasticity and weldability.
The steel plate is widely used in mining, construction, metallurgy, rail transit, machinery manufacturing and other fields. Its strength and durability can effectively extend the life of the equipment, reduce maintenance costs, and improve production efficiency.
Material: Din 1.3401K700 Mn13X120Mn12 high manganese steel plate
- Thickness: 5-100mm
- Width: 1000-2200mm
- Length: 2000-12000mm
- Surface treatment: hot rolling, painting
Mechanical properties
|
Tensile Strength |
Elongation |
20°C Impact Resistance |
Initial Hardness(HB) |
Hardness after Hardened(HB) |
180°old Bending Test |
|
≥900MPa |
≥40% |
ak≥50(J) |
190-250 |
≥300 |
Qualified |
Chemical composition (%)
|
Brand |
C |
Si |
Mn |
P |
S |
|
Mn13 |
0.90-1.20 |
0.30-0.80 |
11.00-14.00 |
≤0.035 |
≤0.030 |
Production process
Application
Quality Inspection
Hot Tags: din 1.3401 k700 mn13 x120mn12 high manganese steel plate, China din 1.3401 k700 mn13 x120mn12 high manganese steel plate manufacturers, suppliers, factory, NM300 Wear Resistant Steel Sheet, Wear Resistant Sheet NM360, Wear NM400 Resistant Sheet, Wear Resistant Steel Plate, NM450 Wear Resistant Sheet, NM500 Resistant Steel Wear Plate