Chemical composition of NM360 wear-resistant steel plate:
Carbon C content: 0.25;
Si content: 0.70;
Mn content: 1.60;
P content: 0.025;
Sulfur S content: 0.015;
Chromium Cr content: 0.80;
Nickel Ni content: 0.50;
Molybdenum Mo content: 0.50;
Ti content: 0.050;
Aluminum Als content: ≥0.010;

Send Inquiry

Product Introduction

NM360 Wear Resistant Steel Plate DIN Cold Rolled Hot Rolled

NM360 wear-resistant plate is a high-strength wear-resistant steel plate, which has a high resistance to wear.

The average hardness of NM360 wear-resistant steel delivered from the factory is 400 HBW, and its mechanical properties are obtained by quenching.

NM360 has been successfully applied in high wear environments, and it also has excellent machinability, especially welding performance.

Examples of NM360 applications include loaders, excavators, dump trucks, transfer equipment, trucks, knife and breaking tools, waste cleaning and recycling equipment, and more.

Delivery condition mechanical properties

hardness

Room temperature hardness: 330-390HBW

Transverse specimen tensile test at room temperature (typical value of 20MM thick steel plate) :

Tensile Strength: 1100 MPa (190 ksi)

Yield point: 900 MPa (145 ksi)

Elongation: 12%(1o=50mm)

Longitudinal sample V notch impact test (typical value of 20MM thick steel plate)

Toughness: -20℃ Akv = 30J

Transverse specimen bending test (typical value of 20MM thick steel plate) :

Formability: bending core diameter > =4.0x specimen thickness bending Angle 180°

Test surface Brinell hardness test once per furnace (40t)