NM500 Abrasion Resistance Plates
NM500 Abrasion Resistance Plates
NM500 Abrasion Resistance Plates
NM500 Abrasion Resistance Plates

NM500 Abrasion Resistance Plates

NM500 Execution standard: GB/T 24186-2009
Class classification :NM500ANM500B
Heat treatment: tempering (quenching + tempering).
Tensile direction: transverse
Tensile strength: ≥1250(1650)
Elongation A50% : ≥8

Send Inquiry

Product Introduction

These plates are popularly used in the mining, quarrying, and construction industry, for applications that entail heavy machinery and equipment operating under extreme wear conditions.

The NM500 abrasion resistance plates are made of low carbon manganese steel with a hardness rating of 500HBW, making them ideal for use in mining trucks, excavators, concrete mixers, and other high-wear equipment. The plates are easy to weld, cut, and form.

The excellent abrasion resistance of NM500 plates is attributed to their microstructure, which consists of hard and tough carbides distributed evenly throughout the steel matrix. These carbides form an interconnected network that resists wear, minimizes chipping and cracking, and ensures good impact resistance.

NM500 abrasion resistance plates offer the following benefits:

1. Long service life
2. Reduced downtime and maintenance costs
3. Increased productivity and efficiency
4. Enhanced safety for workers
5. Impressive value-for-money.

Overall, NM500 abrasion resistance plates are a reliable and cost-effective solution for prolonged wear protection in various industrial applications.

NM	RAEX	Creusabro	XRA	DILLIDUR	Durostat	Hardox
NM500	RAEX500	Creusabro8000	XAR 500	500V	Durostat 500	Hardox500

Abrasion Resistant Steel Plate NM500 Chemical Composition
Heat No.	Grade	C	Si	Mn	P	S	Ni+Mo+Cr	others	CEQ
S21301389	NM500	0.29	0.31	0.99	0.011	0.003	＜2.5	micro	0.71
S11301559	NM500	0.28	0.32	0.97	0.003	0.003	＜2.5	micro	0.71

Abrasion Resistant Steel Plate NM500 Mechanical Properties
Standard		Grade	Thick. / mm	Rm / MPa		A50/ %	Impact T/ ℃	KV2 / J	Hardness /HBW
GB/T 24186-2009		NM500	≤80	≥1200		≥10	--20	≥24	470~530
Plate No.	Heat No.	Grade	Thick. / mm	Re / MPa	Rm / MPa	A50/ %	Impact T/ ℃	KV2 / J	Hardness /HBW
T3111011010	S21300161	NM500	21	1355	1665	9.5	-20	47/53/46	499
Q3331271010	S21300160	NM500	51	1573	1665	13.5	-20	42/44/56	499