Wear Resistant Steel Sheet Plate Mn13
Wear Resistant Steel Sheet Plate Mn13
Wear Resistant Steel Sheet Plate Mn13
Wear Resistant Steel Sheet Plate Mn13

Wear Resistant Steel Sheet Plate Mn13

Material: Mn13X120Mn12DIN1.3401
Thickness: 3mm-200mm
Width: 1000mm-3000mm
Length: 2000mm-12000mm
Surface treatment: hot rolling and cold rolling
Tensile strength: ≥685MPa
Yield strength: ≥430MPa
Elongation: ≥35%
Hardness: HB240-320

Send Inquiry

Product Introduction

Wear resistant steel sheet plate Mn13 is a steel plate with extremely high wear resistance, which is usually used for mechanical equipment and tools with high production process strength requirements. The following are the main specifications of this product:

Material composition: Mn13 is a high manganese steel, containing up to 11-14% manganese, which makes it in a highly wear environment has a strong anti-wear performance, but also can effectively reduce the wear rate of steel plate.
Steel plate thickness: the thickness is usually above 6mm, and the thickest can reach 100mm. The greater the thickness, the better the impact and compression resistance of the steel plate, which is suitable for occasions under a large amount of pressure.
Steel plate width: the width is generally less than 1500mm, suitable for the production of various sizes of parts, convenient processing, manufacturing of various mechanical equipment.
Strength grade: The strength grade of Mn13 steel plate is usually between 400-600MPa, which means that it can withstand large mechanical stress and pressure, and has high durability and reliability.

Chemical composition (%)

Brand	C	Si	Mn	P	S
Mn13	0.90-1.20	0.30-0.80	11.00-14.00	≤0.035	≤0.030

Mechanical properties

Tensile Strength	Elongation	20°C Impact Resistance	Initial Hardness(HB)	Hardness after Hardened(HB)	180°old Bending Test
≥900MPa	≥40%	ak≥50(J)	190-250	≥300	Qualified