The product specifications are listed below:
- 2mm (thickness)
- 6mm (thickness)
-10mm (thickness)
-12mm (thickness)
-15mm (thickness)

Send Inquiry

Product Introduction

NM650 is a high-strength wear-resistant steel plate that has a Brinell hardness of 650HBW. It is mainly used in industries such as mining, construction, and agriculture, where there is a high probability of abrasion. The wear-resistant steel plate has excellent toughness, weldability, and corrosion resistance, making it ideal for harsh environments.

When it comes to installation, the wear-resistant steel plate NM650 is easy to work with, and it can be welded, cut, and drilled with ease. It also has a long service life, reducing the need for frequent replacements and repairs, which can save time and money for the user.

Overall, the NM650 wear-resistant steel plate is an excellent choice for applications that require high abrasion resistance and strength, such as earthmoving equipment, dump truck liners, and other heavy-duty equipment.

Material: low alloy high quality wear-resistant steel NM650.
Quality of hot metal: high purity steel raw materials are required, and the temperature of hot metal is controlled at more than 1500 degrees Celsius.
Performance index: surface hardness of 650HBW or above, high strength, good fracture toughness, strong wear resistance.
Thickness and size: the thickness is generally between 8-120mm, and the width and length also have a certain optional range.
Application field: It is used in fields requiring high strength characteristics such as wear resistance, impact resistance, compressive resistance, tensile strength, such as mining, mining equipment, construction machinery, etc.
Advantages: After processing, it can effectively improve the service life and stability of the equipment, and reduce the downtime and maintenance cost caused by equipment damage.
Precautions: During use, pay attention to the maintenance and maintenance of the surface to prevent the service life from being affected by corrosion and other reasons.

Chemical Composition (%) of NM Wear Resistant Steel

Steel Grade	C	Si	Mn	P	S	Cr	Mo	B	N	H	Ceq
NM360/NM400	≤0.20	≤0.40	≤1.50	≤0.012	≤0.005	≤0.35	≤0.30	≤0.002	≤0.005	≤0.00025	≤0.53
NM450	≤0.22	≤0.60	≤1.50	≤0.012	≤0.005	≤0.80	≤0.30	≤0.002	≤0.005	≤0.00025	≤0.62
NM500	≤0.30	≤0.60	≤1.00	≤0.012	≤0.002	≤1.00	≤0.30	≤0.002	≤0.005	≤0.0002	≤0.65
NM550	≤0.35	≤0.40	≤1.20	≤0.010	≤0.002	≤1.00	≤0.30

Mechanical Properties of NM Wear Resistant Steel

Steel Grade	Yield Strength /MPa	Tensile Strength /MPa	Elongation A50 /%	Hardess (Brinell) HBW10/3000	Impact/J （-20℃）
NM360	≥900	≥1050	≥12	320-390	≥21
NM400	≥950	≥1200	≥12	380-430	≥21
NM450	≥1050	≥1250	≥7	420-480	≥21
NM500	≥1100	≥1350	≥6	≥470	≥17
NM550	-	-	-	≥530	-