NM450 steel plate Mechanical property
Yield strength Re (MPa) : 1000
Tensile strength Rm (MPa) : 1250
Elongation A5:10
Test temperature: 20 (20F)
Impact power Charpy-V longitudinal (J) : 45
Hardness: HBW420-480

Send Inquiry

Product Introduction

AISI wear plate NM450

Steel plate production and cutting process:

Production process: primary refining →LF refining →VD treatment → continuous casting (die casting) → cleaning, heating → rolling → (stacking) → surface inspection → Batch → inspection → Heat treatment → cutting sampling → Performance inspection → storage.

Cutting process: Steel plate factory inspection after the performance indicators meet the requirements in accordance with the cutting processing technology, can be cut processing and drawings, general steel plate thickness is not greater than 20mm, the preferred choice of CNC plasma cutting or CNC laser cutting, if the thickness of the steel plate is greater than 30mm, usually choose CNC flame cutting, you can control the cutting accuracy and time.

Steel Grade	NM360, NM400, NM450, NM500, NM550, NM600,Mn13、
Standard	GB, ASTM, JIS ,DIN, ASTM
Thickness	2mm-300mm
Width	500-2500mm
Length	1000mm-12000mm or according to customer's special request
Tolerance	Thickness: +/-0.02mm, Width:+/-2mm
MOQ	1Tons
Application	1.Automobile, Bridges, Buildings. 2.Machinery, Pressure vessel industries. 3.Ship building, Engineering construction. 4.Mechanical manufacturing, Pavement slab, ect.
Package	Bundle with steel strip,Container shipping
Capacity	2000 tons /month
Mill MTC	can be supplied before shipment
Inspection	The Third Party inspection can be accepted,SGS,BV