X120Mn12 High Manganese Steel Plate MN13 Plate
Thickness: 3mm-200mm
Width: 1000mm-3000mm
Length: 2000mm-12000mm
Surface treatment: hot rolling and cold rolling
Tensile strength: ≥685MPa
Yield strength: ≥430MPa
Elongation: ≥35%
Hardness: HB240-320
X120Mn12, also known as MN13, is a high manganese steel plate with a composition of 1.20% manganese and 12% carbon. It is known for its high strength, toughness, and wear resistance.
The high manganese content in X120Mn12 makes it ideal for applications where abrasion and impact resistance are required, such as in mining equipment, quarrying machinery, and earthmoving equipment. The high carbon content also provides good hardness and strength, making it suitable for use in applications requiring high strength and durability.
The X120Mn12 High Manganese Steel Plate is available in different sizes and thicknesses, making it suitable for a wide range of applications. It can be cut, welded, and formed into various shapes and sizes to meet the specific requirements of different industries.
Mechanical properties
|
Tensile Strength |
Elongation |
20°C Impact Resistance |
Initial Hardness(HB) |
Hardness after Hardened(HB) |
180°old Bending Test |
|
≥900MPa |
≥40% |
ak≥50(J) |
190-250 |
≥300 |
Qualified |
Chemical composition (%)
|
Brand |
C |
Si |
Mn |
P |
S |
|
Mn13 |
0.90-1.20 |
0.30-0.80 |
11.00-14.00 |
≤0.035 |
≤0.030 |
Production process
Application
Quality Inspection
Hot Tags: x120mn12 high manganese steel plate mn13 plate, China x120mn12 high manganese steel plate mn13 plate manufacturers, suppliers, factory, NM300 Wear Resistant Steel Sheet, Wear NM400 Resistant Sheet, Wear Resistant Steel Plate, NM450 Wear Resistant Sheet, Wear Resistant Sheet NM360, NM650 Wear Resistant Steel Plate