Chemical composition (%) : Carbon C: 0.57 ~ 0.65 Silicon Si: 0.17 ~ 0.37 Manganese Mn: 0.50 ~ 0.80 Sulfur S: ≤0.035 P: ≤0.035 Chromium Cr: ≤0.25 Nickel Ni: ≤0.25 Copper Cu: ≤0.25

Send Inquiry

Product Introduction

C60 round bar refers to a cylindrical bar made of C60 steel. These bars are used in various industrial applications such as construction, automotive, and aerospace industries. They are versatile, durable, and offer excellent strength and toughness, making them a popular choice in demanding environments. C60 round bars are available in various sizes, lengths, and finishes to meet specific requirements.

The following are the product specifications of C60 round steel:

Diameter: from 5 mm to 500 mm, according to customer needs can be customized special size.
Length: usually 3 meters to 6 meters, can also be made according to customer requirements of different lengths.
Material: The use of high-quality carbon structural steel, with high strength and high hardness, strong wear resistance, easy processing and other characteristics.
Surface treatment: usually through sandblasting, painting and other treatment methods, so that the surface is smooth and bright, strong corrosion resistance.
Application fields: Widely used in the manufacture of machine parts, automotive parts and engineering parts, etc., with a wide range of application prospects and market demand.

C-60 Equivalent grades:

USA	UK	China	Japan	Australia
1060	070M60	60#	S60C	1060

C-60 Chemical composition:

The following table shows the chemical composition of C60 steel:

Grade	C	Mn	P	S	Si	Cr	Mo	Ni	Cr+Mo+Ni
C60/1.0601	0.57-0.65	0.60-0.90	≤ 0.045	≤ 0.045	≤ 0.4	≤ 0.4	≤ 0.1	≤ 0.4	≤ 0.63
C60E/1.1221	0.57-0.65	0.60-0.90	≤ 0.03	≤ 0.035	≤ 0.4	≤ 0.4	≤ 0.1	≤ 0.4	≤ 0.63
C60R/1.1223	0.57-0.65	0.60-0.90	≤ 0.03	0.02-0.04	≤ 0.4	≤ 0.4	≤ 0.1	≤ 0.4	≤ 0.63

C-60 Mechanical Properties:

Mechanical properties a at room temperature in the quenched and tempered condition (+QT)
Diameter d mm	≤ 16	16-40	40-100
Thickness t mm	< 8	8-20	20-60
Yield Strength Mpa	≥580	≥520	≥450
Tensile Strength Mpa	850-1000	800-950	750-900
Elongation, %	≥11	≥13	≥14
Reduction of area ,%	≥25	≥30	≥35

Mechanical properties a at room temperature in the normalized condition (+N)
Diameter d mm	≤ 16	16-100	100-250
Thickness t mm	≤ 16	16-100	100-160
Yield Strength Mpa	≥380	≥340	≥310
Tensile Strength Mpa	≥710	≥670	≥650
Elongation, %	≥10	≥11	≥101

C-60 Physical Properties:

Physical Properties	Metric	Imperial
Density	7.85 g/cm3	0.284 lb/in3

PRODUCTION PROCESS

EN 1.0601 (C60) Non Alloy Steel

Product Application

EN 1.0601 (C60) Non-Alloy Steel

Hot Tags: c60 round bar, China c60 round bar manufacturers, suppliers, factory, Cold Rolled High Carbon Steel Coil, Cold Drawn Steel Round Bar, Carbon Steel Round Bar C60, Cold Drawn Steel Bar, 65Mn Spring Steel Round Bar, S20C Carbon Steel

1.0601 Alloy Steel Bar C60 Steel Bar

EN 1.0601 (C60) Non Alloy Steel

C60 Round Bar

C-60 Equivalent grades:

USA

UK

China

Japan

Australia

1060

070M60

60#

S60C

1060

C-60 Chemical composition:

The following table shows the chemical composition of C60 steel:

Grade

C

Mn

P

S

Si

Cr

Mo

Ni

Cr+Mo+Ni

C60/1.0601

0.57-0.65

0.60-0.90

≤ 0.045

≤ 0.045

≤ 0.4

≤ 0.4

≤ 0.1

≤ 0.4

≤ 0.63

C60E/1.1221

0.57-0.65

0.60-0.90

≤ 0.03

≤ 0.035

≤ 0.4

≤ 0.4

≤ 0.1

≤ 0.4

≤ 0.63

C60R/1.1223

0.57-0.65

0.60-0.90

≤ 0.03

0.02-0.04

≤ 0.4

≤ 0.4

≤ 0.1

≤ 0.4

≤ 0.63

C-60 Mechanical Properties:

Mechanical properties a at room temperature in the quenched and tempered condition (+QT)

Diameter d mm

≤ 16

16-40

40-100

Thickness t mm

< 8

8-20

20-60

Yield Strength Mpa

≥580

≥520

≥450

Tensile Strength Mpa

850-1000

800-950

750-900

Elongation, %

≥11

≥13

≥14

Reduction of area ,%

≥25

≥30

≥35